15/06/2016 admin

NON-ASBESTOS PACKING

SN 1688 PURE PTFE WITH LUBRICANT : DESCRIPTION 
  Braided with PTFE fibre yarn braided and treated with high temperature resistant lubricants, minimizing shaft worn-out due to best self-lubricant applicable for dynamic seal at high linear speed.
  SERVICE:
  Pressure  : 15 MPA
  Shaft Speed : 0-10 (M/S)
  Temperature : -200  to 260 ˚C
  pH  Range : 0 - 14

Download Spec :  SN 1688 PURE PTFE WITH LUBRICANT

SN 1689 PURE PTFE (OIL FREE) : DESCRIPTION
  Braided with PTFE fibre yarn oil free braided and treated, minimizing shaft worn-out due to best self-lubricant applicable for dynamic seal at high linear speed.
  SERVICE  :
  Pressure  : 15 MPA
  Shaft  Speed : 0-10 (M/S)
  Temperature : -200  to 260 ˚C
  pH  Range : 0 - 14

Download Spec : SN 1688 PURE PTFE (OIL FREE)

SN1699 SYTHETIC WITH PTFE  : DESCRIPTION 
  Made from polyacylonitrile yarns, Where each strand is impregnated in a unique way with PTFE dispersion.  This packing is then re-impregnated with PTFE dispersion and mineral lubricants for a good running-in period
  SERVICE  :
  Pressure  : 20 Mpa
  Shaft Speed : 12 (m/s)/Rotary
  Temperature : -50  to 260 ˚C
  pH  Range : 2 - 12

Download :  SN1699 SYTHETIC WITH PTFE

SN7101 RAMIE WITH PTFE  : DESCRIPTION 
  Made from RAMIE yarns, Where each strand is impregnated in a unique way with PTFE dispersion.  This packing is then re-impregnated with PTFE dispersion and mineral lubricants for a good running-in period.
  SERVICE  :
  Shaft Speed : 10 (m/s)/Rotary
  Temperature :  -50  to 260 ˚C
  pH  Range : 4- 12

Download Spec : SN7101 RAMIE WITH PTFE

SN4001 PURE KEVLAR : DESCRIPTION
  Made of pure Kevlar aramid fiber yarn and impregnated with PTFE , having strength, module of Kevlar rope is as high as the steel-like strength. Kevlar packing seal can resist more serve media and high pressure .
  SERVICE  :
  Pressure  : 25 Mpa
  Shalft Speed : 0-15 m/s
  Temperature :  -100 ~ +280 Cͦ
  pH  Range : 2 – 12

Download Spec :  SN4001 PURE KEVLAR

SN1690 PTFE GRAPHITE : DESCRIPTION 
  The packing is braided from GPTFE yarns. Its consistently high thermal conductivity ensures an effective seal, especially at high temperature and speeds. There are no free graphite particles on the surface therefore little contamination would occur.
  SERVICE  :
  Pressure     :  Rotating         2.0 MPA(20 bar)
                          :  Reciprocating 20 MPA(200 bar)
                          :  Valve           15 MPA(150 bar)
  Linear Speed : 0-18 m/s  Rotory
  Temperature : -200  to 280 ˚C
  pH  Range : 0 ~ 14

Download Spec :  SN1690 PTFE GRAPHITE

SN3906 CARBON GRAPHITE : DESCRIPTION 
  Made of carbon fiber impregnated with fine Graphite powder and applying of lubricants having strength and modulus, good self lubricant .
  SERVICE  :
  Pressure  : 25 Mpa
  Shaft Speed : 0-20 (m/s)
  Temperature : -200~+650Cͦ (STEAM)
  pH  Range : 0 - 14

Download Spec :  SN3906 CARBON GRAPHITE

SN6006 PURE GRAPHITE : DESCRIPTION 
  Made of expanded graphite packing is braided from high-grade expanded graphite yarn. Suitable for  resistance from high temperature and chemical corrosion, as well as other special sealing effects.
  SERVICE  :
  Pressure  : 25 Mpa
  Shaft Speed : 0-8 (m/s)
  Temperature : -200~+650Cͦ (STEAM)
                               : -200~+565Cͦ Cͦ (ATMOSPHERE)
  pH  Range : 0 - 14

Download Spec :  SN6006 PURE GRAPHITE

SN6006 IN PURE GRAPHITE WITH INCONEL : DESCRIPTION 
  Made of expanded graphite packing  with  Inconel wire reinforcement  is braided from high-grade expanded graphite yarn. Suitable for  resistance from high temperature, high pressure  and chemical corrosion, as well as other special sealing effects.
*Only used in valve and static sealing .
  SERVICE  :
  Pressure  : 30 Mpa
  Temperature : -200~+650Cͦ (STEAM)
                               :-200~+565 Cͦ (ATMOSPHERE)
  pH  Range : 0 - 14

Download Spec :  SN6006 IN PURE GRAPHITE WITH INCONEL